CORROSION PREVENTION MANUAL VOLUMES 1 AND 2 INTRODUCTION
V8F610 UNION OIL CO. OF CALIFORNIA 2901 WESTERN AVE. SEATTLE, WA 98111
V8H761 GETTY OIL CO. 200 EAST CENTRAL EL DORADO, KS 67042-2130
V8P482 AIR BP PRIMARY ROAD HOPKINS INTERNATIONAL AIRPORT CLEVELAND, OH 44135-3194
V86192 CLEMCO INDUSTRIES P. 0. BOX 7680 SAN FRANCISCO, CA 94120
V86961 SHELL CHEMICAL CO. DIV. OF SHELL OIL CO. ONE SHELL PLAZA, P. O. BOX 2463 HOUSTON, TX 77001
V9V291 ASHLAND PETROLEUM CO., DIV. OF ASHLAND OIL, INC. 1409 WINCHESTER AVE., P. O. BOX 391 ASHLAND, KY 41114
V98308 CASTROL, INC. 1925 N. MARIANNA AVE. LOS ANGELES, CA 90032-4007
Volume 1
INTRODUCTION
Page 7 OCT 01/01
THIS PAGE INTENTIONALLY LEFT BLANK
Volume 1
INTRODUCTION
Page 8
OCT 01/01
1. General
A. The ability to recognize corrosion in its early stages is required to enable
corrective action to be taken before costly repairs or replacements become
necessary.
2. Identification
A. Aluminum Alloys --Corrosion of the aluminum surface is usually indicated by
whitish powdery deposits with dulling of the surface on unpainted parts. The
white powdery deposit also forms at discontinuities in protective coating
and may spread beneath paint causing blistering or flaking. As the corrosion
attack advances, the surface will appear mottled or etched with pitting.
Swelling or bulging of skins or pulled or popped rivets are often visual
indications of corrosions.
B. Alloy and Carbon Steels -- Corrosion is indicated by red rust deposits and
pitting of the affected surfaces.
C. Corrosion Resistant Steels -- Corrosion is indicated by black pits or a uni-form reddish-brown surface.
3. Types
A. The terminology used in describing corrosion is based on either the appear-ance of the corrosive attack or the mechanism associated with its formation.
Frequently, several types of corrosion will occur simultaneously and it
becomes difficult to determine the specific cause.
B. The following types of corrosion are those most commonly experienced:
(1)Surface Corrosion --Visible as uniform etching of the metal surface,
and results from direct chemical attack.
(2)Pitting --Detected as a series of pits on the metal surface, usually in
small, well-defined local areas (Fig. 1).
(3)Exfoliation -- Inter granular corrosion characterized by bulging or
blistering of the metal surface, resulting from the force created by
expanding corrosion products at the grain boundaries (Fig. 2).
(4)Galvanic --Usually visible as pitting and is often referred to as dis-similar metal corrosion. However, it is not limited to just dissimilar 中國航空網 m.k6050.com 航空翻譯 www.aviation.cn 本文鏈接地址：757 防腐手冊 CORROSION PREVENTION MANUAL 第二冊 一般信息(8)